HyboFOAM® A
Introduction
HyboFOAM® A is a closed-cell rigid foam based on polymethacrylimide (PMI), which contains no halogen at all. The cell size is coarse and uniform.
After different heat treatment processes, it can be divided into conventional and HT series, and the HT series has better high-temperature creep resistance.
Structural Foam For Aircraft
HyboFOAM® A manufacturing meets the material specification CMS-CP-403 requirements of COMAC and is mainly used for high-grade composite material components, such as aircraft, aerospace/launch vehicles, drones, etc.
Product Parameters
Property | Test Method * | Unit | HyboFOAM® | HyboFOAM® | HyboFOAM® | HyboFOAM® |
A 52 | A 75 | A 110 | A 110-HT | |||
Density | GB/T 6343 | kg/m³ | 52 | 75 | 110 | 110 |
ASTM D1622 | g/cm³ | 0.052 | 0.075 | 0.11 | 0.11 | |
ISO 845 | Ib/ft³ | 3.245 | 4.68 | 6.87 | 6.87 | |
Compressive Strength | GB/T 8810 ASTM D1621 ISO 844 |
MPa | 1 | 1.8 | 3.5 | 3.5 |
psi | 145 | 261 | 508 | 508 | ||
Compressive Modulus | MPa | 45 | 85 | 140 | 140 | |
psi | 6525 | 12325 | 20300 | 20300 | ||
Tensile Strength | GB/T 110040.2 AST M6vwD638 ISO 527-2 |
MPa | 1.9 | 2.8 | 4.5 | 4.5 |
psi | 276 | 406 | 653 | 653 | ||
Tensile Modulus | MPa | 70 | 115 | 160 | 160 | |
psi | 10150 | 16675 | 23200 | 23200 | ||
Elongation at Break | % | 3.5 | 3.5 | 3.5 | 3.5 | |
Shear Strength | GB/T 1455 ASTM C273 DIN 53294 |
MPa | 0.85 | 1.35 | 2.5 | 2.5 |
psi | 123 | 196 | 363 | 363 | ||
Shear Modulus | MPa | 25 | 40 | 60 | 60 | |
psi | 3625 | 5800 | 8700 | 8700 | ||
Heat Deflection Temperature | GB/T 31295 | ℃ | ≥180 | ≥200 | ||
DIN 53424 | ||||||
The above values are typical values for nominal density, and the measured values will vary due to manufacturing deviations. * Data is based on ASTM standard test methods, but GB or ISO values can be confirmed upon request. |
Processing and Production
HyboFOAM® A can withstand a medium temperature curing process with a maximum temperature of 180 ℃ and a maximum pressure of 0.7 MPa, depending on the density. Suitable for curing methods such as autoclave, vacuum bag, RTM, VARTM, VARI, HP-RTM, etc.
Due to its excellent surface resin absorption, engineers can find a perfect balance between peel strength and lightweight requirements.
Thermoforming and Shaping
To meet different dimension parts and geometry, it is very easy to shape HyboFOAM® A by thermo-shaping, bonding by various adhesive, and common CNC machine.
HYBO can also directly provide high-precision preformed or ready to use foam core materials with complex or simple geometric shapes.
More Information
If you have questions or want to discuss the use of HyboFOAM® A in your application, we recommend that you communicate with your local contacts.
Please visit www.hybofoam.com, find and contact the local contact person directly by phone or email.
HYBO(Fujian)New Material Technology Ltd.,
HyboFOAM® is a registered trademark of HYBO.
The above information, as well as all technical and other suggestions, are based on HYBO's existing knowledge and experience. However, HYBO assumes no liability for such information or advice, including the extent to which such information or advice may relate to third party intellectual property rights.
HYBO reserves the right to change information or recommendations at any time without notice. HYBO disclaims all express or implied representations and warranties, and assumes no responsibility for the merchantability of the product or its suitability for a specific purpose (even if HYBO is aware of the purpose) or otherwise.
HYBO is not responsible for any form of indirect, indirect or incidental damages (including loss of profits). The customer is fully responsible for arranging qualified experts to inspect and test all products. The mention of product names used by other companies is neither a recommendation nor recognition of the corresponding products, and does not mean that similar products cannot be used.